<thead id="jv797"><cite id="jv797"></cite></thead>
    <noframes id="jv797"><cite id="jv797"><output id="jv797"></output></cite><listing id="jv797"></listing>

        <address id="jv797"><del id="jv797"><p id="jv797"></p></del></address>

            <b id="jv797"><cite id="jv797"></cite></b>
              <rp id="jv797"></rp>
              <delect id="jv797"></delect>
              <nobr id="jv797"><del id="jv797"><font id="jv797"></font></del></nobr>

              <strike id="jv797"></strike>

              <listing id="jv797"><ruby id="jv797"><delect id="jv797"></delect></ruby></listing>

              <listing id="jv797"><rp id="jv797"><ruby id="jv797"></ruby></rp></listing>

              <ol id="jv797"><ol id="jv797"></ol></ol>

                <var id="jv797"></var>

              <dfn id="jv797"><del id="jv797"></del></dfn>
              <b id="jv797"><del id="jv797"></del></b>

              鋼材料的鑄造性、鍛性、焊接性和冷彎性

              發布者: 發布時間:2016/5/25 10:12:43 閱讀:次 【字體:

                  做鋼結構工程在材料的選擇上一定要特別注意,下面就是重慶鋼結構工程介紹的關于鋼材料的幾大特性。

                1. 鑄造性 金屬材料能用鑄造方法獲得合格鑄件的能力稱為鑄造性。鑄造性包括流動性、收縮性和偏析傾向等。流動性是指液態金屬充滿鑄模的能力,流動性愈好,愈易鑄造細薄精致的鑄件,收縮性是指鑄件凝固時體積收縮的程度,收縮愈小,鑄件凝固時變形愈小。偏析是指化學成分不均勻,偏析愈嚴重,鑄件各部位的性能愈不均勻,鑄件的可靠性愈小。

                2. 鍛性 鍛性是材料在承受錘鍛、軋制、拉拔、擠壓等加工工藝是會改變形狀而不產生裂紋的性能。它實際上是金屬塑性好壞的一種表現,金屬材料塑性越高,變形抗力就越小,則鍛性就越好。鍛性好壞主要決定于金屬的化學成分、顯微組織、變形溫度、變形速度及應力狀態等因素。

                3. 焊接性 焊接性是指金屬在特定結構和工藝條件下通過常用焊接方法獲得預期質量要求的焊接接頭的性能。焊接性一般根據焊接時產生的裂紋敏感性和焊縫區力學性能的變化來判斷。

                4. 冷彎性 金屬材料在常溫下能承受彎曲而不破裂的性能,稱為冷彎性。出現裂紋前能承受的彎曲程度愈大,則材料的冷彎性能愈好